Current Location： Home > Spot Mall > Polyether polyol > Special varieties Polyether 10LD28Z

Special varieties Polyether 10LD28Z (Special varieties Polyether 10LD28Z)

Bargaining 10-21 09:11 Update

Inquiry

Whatsapp:
+86 19117288062

Contact person： Chemwin

Phone： +86 19117288062

Special varieties Polyether 10LD28Z

Warehouse

Services Merchant Delivery

Payment Method T/T ; L/C ;

Shipping Fee Place of delivery： Need to ask for quotation with the seller

Specification weight

Total Selected{{ form.amount }}Pieces {{ form.amount }} Total￥{{ form.price * form.amount }}

Information View:

Chinese

English

Product Description

Nature Description

Hydroxyl value (mgKOH/g):22.0-26.0 moisture (%):≤ 0.10PH:6.5-10 viscosity (mPa · s/25℃):1800-2500 solid content: 29-33% functionality: 3

Product Applications

It is used for flame retardant high resilience foam, cold molded soft foam, semi-rigid foam, self-skinning foam, reaction injection molded products and other materials. Structural flame retardant polymer polyol has better flame retardant and reaction fluidity compared with ZR-001; It has better adaptability under the condition of low mold temperature.

Security

Storage conditions： When transporting 10LD28Z, it should be strictly protected against rain and dirt, and be careful to handle it to prevent leakage caused by collision with hard objects. When storing 10LD28Z, it should be stored at room temperature in a ventilated and dry warehouse to avoid being in a humid environment, and the storage temperature should be kept below 50℃, so as to avoid sun exposure, away from water sources, heat source. Or sealed storage in containers made of steel, aluminum, polyethylene or polypropylene. To prevent moisture absorption and oxidation, it is recommended to fill the containers with nitrogen. If the storage temperature is higher than 60℃, the product quality will decrease. Short-term heating or cooling has little effect on the quality of the product, but attention should be paid to the obvious increase in viscosity when the product is at a lower temperature, this situation may bring some difficulties to the production and processing process.